Name Thomas temperature glue (THO4052) 
 Overview of the strains epoxy adhesives, two component, room temperature fast curing, high adhesion strength, good temperature resistance, easy to operate. 
 Scope for work under conditions of high temperature metals, ceramics, composite materials, self-adhesive and stick each other, but also a variety of containers for leaks, cracks in cylinder block, casting bonding, filling, sealing, plugging, and repair and electrical , instrument heat bonding and sealing components. 
 Sex 

 Can 

 Special 

 ? A component for point light (more colors) viscous liquid without solid particles. Group B were as pale yellow liquid. 
 ? Fast cure, 25 ℃, 1-3 hours early, when cure, 18 hours close to the maximum bond strength. 
 ? High bonding strength, durability, UV resistance and excellent performance. 
 ? heat resistance, and adapt to a wide range of temperatures, at higher temperatures there is still a good bonding results. 
 ? adhesive surface is not strictly, the two groups were in proportion to deploy, easy to use. 
 ? excellent resistance to media, oil, water, acid, kerosene, alcohol, alkali, heterocyclic hydrocarbons, nuclear radiation. 
 ? Safety and toxicity characteristics: a very slight smell, no inhalation hazard, actual non-toxic after curing. 
 ? good storage stability, storage for one year. 
 The main technical performance indicators are as follows: 
 Temperature range: -40 - +380 ℃ 
 Bond strength: room temperature: Tensile strength ≥ 25MPa; shear strength ≥ 20 MPa 
 150 ℃: tensile strength of 3-5 MPa 
 Use 
 Method 1 will be sticky rust, dirt, wipe. 
 2, A, B component and mix thoroughly by 10:1.2-1.5 ratio after full use. 
 3, is tuned to the glue applied to the adherend surface, close up, compaction, standing 2 to 4 hours. 
 Note 
 Items 1, can not take the plastic tool mix. 
 2, the operating environment ventilation. 
 3, glue such as contact with skin, wash with soap and water can be timely. 
 4, unused plastic should be covered and placed in a cool ventilated place. 